Adsorption of phenol and aniline onto original and with quaternary ammonium salts (QASs)-modified montmorillonite was described by sorption isotherms of type III and II, respectively. For the montmorillonite (MMT) modification - hydrophobisation, cetyltrimethyl- ammonium (CTMA) and tetramethylammonium (TMA ) cations were used. In comparison with phenol, aniline was adsorbed largely on original MMT but less on modified one. XRD pa tterns indicated that both aromatic compounds were intercalated in the MMT interlayer be ing perpendicularly oriented to silicate sheets. Alkyl chains of CTMA and TMA probably act as organic "pillars" stabilising the MMT tabular structure against exfoliation due to the intercalation with phenol and aniline of high concentrations., Hana Kostelníková, Petr Praus and Martina Turicová., and Obsahuje bibliografické odkazy
The intercalation of organic anions, namely acrylate, methacrylate, 2-acrylamido-2-me thyl-1-propanesulfonate (AMPS), 4-vinylbenzoate, and 4,4’-azobis(4-cyanopentanoate) into Mg-Al and Zn-Al layered double hydroxides (LDHs) was studied. The coprecipitated Mg-Al-NO 3 and Zn-Al-NO 3 hydrotalcite-like compounds with M II /Al molar ratio of 2 were used as precursors. The anion exchange and rehydration of calcined LDH precursors were applied for the intercalation. The anion exchange appeared to be the most effective method; all examined organicanions were intercalated successfully by this way both in Mg-Al and Zn-Al host structur es. The intercalated LDHs were us ed as comonomer and initiator for preparation o f LDH/polymethacrylate nanocomposites: mixture of monomer and LDHs intercalated with organic anions were dispersed in aqueous phase and then the emulsion polym erization was performed in the presence of inorganic (nano)particles to obtain polybutylmethacrylate hybrid latexes. Na nostructured hybrid materials containing a low amount (1 - 3 wt%) of inorganic nanofiller were prepared. Particles with size of 60 - 100 nm were detected by dynamic light scattering and small-angle X-ray scattering methods. Furthermore, a hydrophobization of LDH nanof illers with dodecylsulfate (DS) was tested in order to facilitate their dispersion in the polymer matrix. A minor part of AMPS anions was incorporated into Mg-Al-DS LDH during anion exchange in the aqueous solution containing AMPS. Us ing Mg-Al-DS LDH modified w ith AMPS, the nanocomposites were obtained by emulsion polymerization and also by the solution polymer ization in 1-methyl-2-pyrolidone., František Kovanda, Eva Jindová, Barbora Doušová, David Koloušek, Josef Pleštil and Zdeňka Sedláková., and Obsahuje bibliografické odkazy